Fabric Coating Polyamide Hot Melt Adhesive 110C - 120C PA Polyamide Granule
|
Fabric Coating Polyamide Hot Melt Adhesive 110C - 120C PA Polyamide Granule
| Place of Origin | Nantong Jiangsu |
| Brand Name | JCC |
| Certification | Oeko-tex；ISO；ZDHC |
| Model Number | JCC-PA 2080 |
| Document | Polyamide PA hot melt adhes...ve.pdf |
Product Details
Shelf Life:
12 Months
Color:
Amber
Application:
For Fabric Coating
Form:
Granule
Type:
Thermoplastic
Feature:
Flexible; Low Temperature Resistant
Press Temperature:
110-120℃
Highlight:
fabric coating Polyamide Hot Melt Adhesive
,Polyamide Hot Melt Adhesive 120C
,fabric coating PA polyamide granule
Payment & Shipping Terms
Minimum Order Quantity
1000
Price
$3.5-4.5/kg
Packaging Details
20kg/bag; 1000kg/pallet
Delivery Time
7-15 work days
Payment Terms
L/C,D/P,T/T
Supply Ability
2000tons/month
Product Description
JCC High-Performance Modified PA Polyamide Granule for Fabric Coating
Product Specifications
| Attribute | Value |
|---|---|
| Shelf Life | 12 months |
| Color | Amber |
| Application | For fabric coating |
| Form | Granule |
| Type | Thermoplastic |
| Feature | Flexible; low temperature resistant |
| Press temperature | 110-120℃ |
Product Overview
JCC Modified PA (Polyamide) Granules are high-performance adhesive materials designed for fabric coating and finishing processes. These modified polyamide granules provide excellent adhesion, high flexibility, and durability, making them ideal for bonding, laminating, or coating textiles in apparel, industrial fabrics, and technical textiles.
Key Features
- Material Base: Modified Polyamide (PA)
- Form: Granule for hot-melt or extrusion coating
- Application: Fabric coating, lamination, and bonding
- Properties: Strong adhesion, heat and wear resistance, high flexibility
- Compatibility: Suitable for natural and synthetic fabrics, nonwoven materials, and composite textiles
Typical Applications
- Coating fabrics for waterproof, protective, or decorative finishes
- Laminating textiles with functional or composite layers
- Bonding interlining, reinforcement layers, or decorative films on fabrics
- Hot-melt extrusion or industrial coating processes
Performance Benefits
- Provides uniform and durable coating layers
- Maintains flexibility and tensile strength of the fabric
- Heat and chemical resistant, suitable for industrial textile applications
- Compatible with automated coating and lamination lines
Technical Specifications
| Characteristic | Range/Typical Value |
|---|---|
| Appearance | Amber Granule |
| Chemical Composition | Modified Copolyamide |
| Density (g/cm³) | 0.92~0.98 |
| Melting Index (g/10min) | 45~75 (140℃,2.16kg) |
| Melting Range DSC (℃) | 48~82 |
| Glass Transition Temperature (℃) | 0 |
| Softening Point (℃) | 98 |
| Viscosity (mPa*s@200℃) | 15000 |
| Washing resistance (℃) | 40 |
Directions for Use
- The surface should be clean, dry and free of solvent or grease. Low surface/environment temperature of the substrate may cause early adhesive condensation, open time shortening and even adhesive falling off. If necessary, preheat the adhesive.
- Operate above 110℃ with 1-3 kg pressure to the substrate for 10-20 seconds to complete the bonding.
- After bonding, it will achieve the final strength after complete crystallization at room temperature (25℃).
Frequently Asked Questions
What are modified polyamide granules for fabric coating?
Modified polyamide (PA) granules for fabric coating are hot-melt PA particles designed for textile coating, laminating, and bonding. When heated, they melt and form a uniform, durable coating or adhesive layer on fabric surfaces.
What are the main materials and features of the granules?
- Modified Polyamide (PA): High temperature resistance, flexibility, and strong adhesion
- Hot-melt granules: Easy to melt for coating or heat-press applications
- Wide applicability: Suitable for natural fibers, synthetic fibers, and composite materials