PA Powder Copolyamide Hot Melt Adhesive Powder For Garment Interlining
| Place of Origin | Nantong Jiangsu |
| Brand Name | JCC |
| Certification | Oeko-tex；ISO；ZDHC |
| Model Number | JCC-PA 6150 |
| Document | Copolyamide products.pdf |
garment interlininghot melt adhesive powder
,White hot melt adhesive powder
,White eva hot melt adhesive
| Attribute | Value |
|---|---|
| Shelf Life | 12 months |
| Color | White |
| Application | For garment interlining |
| Form | Powder |
| Type | Thermoplastic |
| Feature | Balance between performance and price |
| Advantage | Economical, suitable for mass-market apparel production |
This economical PA powder is a cost-effective hot melt adhesive solution specially developed for garment interlining applications. Designed to offer a balance between performance and price, it delivers reliable bonding strength, soft hand feel, and adequate washing resistance—making it ideal for mass-market apparel production.
The powder is suitable for powder scatter coating, dot printing, or mesh lamination, and works well with a wide range of fabrics such as cotton, polyester, viscose, and blended woven or knitted textiles.
- Economical formulation for large-scale interlining use
- Good adhesion to common fabrics used in garment construction
- Soft hand feel and good fabric drape
- Medium wash resistance (suitable for standard garment care)
- Compatible with dot coating and scatter coating processes
- Available in multiple particle size options
| Range/Typical Value | |
|---|---|
| Appearance | White powder |
| Chemical Composition | Copolyamide |
| Density (g/cm3) | 1.0-1.1 |
| Melting Range DSC (℃) | 110-133 |
| Melt Flow(g/10min@160℃) | 36-47 |
| Glass Transition Temperature (℃) | 25 |
| Hardness(HD before crystallization) | 74 |
| Hardness(HD after crystallization) | 81 |
- The surface should be clean, dry and free of solvent or grease. Low surface/environment temperature of the substrate may cause early adhesive condensation, open time shortening and even adhesive falling off. If necessary, preheat the adhesive.
- Operate above 140℃ with 1-3 kg pressure to the substrate for 10-20 seconds to complete the bonding.
- After bonding, it will achieve the final strength after complete crystallization at room temperature 25℃.
It is a cost-effective copolyamide hot melt adhesive powder designed primarily for bonding garment interlining fabrics, providing reliable adhesion with a soft hand feel suitable for everyday apparel manufacturing.
It bonds well to common interlining substrates including cotton, polyester, viscose, and their blends in woven or knitted forms.
CONTACT US AT ANY TIME