| Place of Origin: | Nantong Jiangsu |
| Brand Name: | JCC |
| Certification: | Oeko-tex Certificate, ISO, ZDHC |
| Model Number: | JCC-TPU F695T |
JCC TPU film polyurethane hot melt adhesive is a high-performance bonding solution specifically engineered for use in automotive seat ventilation systems. This adhesive film provides excellent flexibility, strong adhesion, and heat resistance, making it ideal for bonding various layers of materials used in ventilated car seats, such as perforated leather, foam layers, air channels, and spacer fabrics.
Designed for automated lamination processes, the hot melt glue activates upon heating, forming a durable and stable bond without solvents. Its TPU-based formulation ensures long-term durability, resistance to wear and tear, and compatibility with automotive-grade materials.
| Item | Range |
|---|---|
| Appearance | Nature color adhesive film |
| Hardness (Shore A) | 90 |
| Density (g/cm³) | 1.1-1.12 |
| Elongation at break (%) | >550 |
| Tensile strength (Mpa) | >30 |
| Tear strength (N/mm) | >100 |
| Melting range (°C) | 190~200 |
| Burning speed (mm/min) | <80 |
0.025mm and 0.065mm thickness are currently available. Different thickness can be customized.
Applied by high frequency welding.
TPU film is a non-hazardous item and should be handled with care during transportation. Avoid exposure to sunlight, rain, heat, or heavy pressure. Do not use hooks during loading and unloading to protect the packaging. The product must be stored in a cool, well-ventilated, dry place, protected from sunlight, rain, and high temperatures. Stacking height should not exceed three layers. The storage environment should be between 0°C and 30°C in a cool, dry place (humidity ≤ 70% RH).
Shelf Life: 12 months from the date of production.
This JCC TPU hot melt adhesive film is suitable for bonding a wide range of materials commonly used in automotive seat ventilation systems, including genuine leather, synthetic leather, foam, non-woven fabric, spacer mesh fabric, and TPU film. It offers excellent compatibility and strong adhesion.
It is polyether based.